단종 AL5697 (단종) 알루미나 티타니아 분말 (Al2O3 13TiO2)

These powders, comprising alumina and approximately 13% titania (nominal), are formulated to create dense ceramic coatings with exceptional wear resistance, allowing for excellent surface finishes upon grinding. Compared to coatings of alumina with 13% titania or pure alumina, these materials generally exhibit higher toughness but lower hardness, dielectric strength, and somewhat reduced resistance to chemical corrosion. Operational temperatures of up to 540°C (1000°F) are viable for these coatings. Alumina Titania Powder (Al2O3 13TiO2) is particularly recommended for its resistance against abrasive grains, hard surfaces, fibers, threads, fretting, cavitation, and particle erosion. It finds applications in various fields including printing ink transfer rolls, textile components, petrochemical equipment (pump sleeves), mechanical seals, and electrical insulators.

Alumina Titania Powder (Al2O3 13TiO2) Specifications:

Alumina Titania Powder (Al2O3 13TiO2) Applications:

1. Textile components: In textile machinery, this coating can be used to improve the wear resistance and durability of components, ensuring the stability and long-term operation of the production line.

2. Petrochemical applications: For example, coatings are used on equipment such as pump bushings to enhance their wear resistance and chemical stability, ensuring reliable operation of the equipment under harsh conditions.

3. Mechanical seals: This coating can be used on mechanical seals to improve their wear resistance and sealing performance, thus extending the service life of the equipment.

4. Electrical insulating materials: Due to their chemical stability and wear resistance, this coating is suitable for electrical insulating materials, for example for applications such as insulators.

Alumina Titania Powder (Al2O3 13TiO2) Packing:

Our Alumina Titania Powder (Al2O3 13TiO2) is carefully handled during storage and transportation to preserve the quality of our product in its original condition.

FAQs

Q1: What is Alumina Titania Powder (Al2O3 13TiO2)'s composition ratio and performance advantages?

A1: The composition is 87% Al₂O₃ + 13% TiO₂. The high titanium content significantly improves the toughness and thermal shock resistance of the coating, which is suitable for high-impact and strong corrosive conditions.

Q2: What are the advantages compared with low titanium content (e.g. 3% TiO₂) powders?

A2.

Increased toughness: 20% increase in flexural strength (vs. 3% TiO₂)

Bond strength: ≥45 MPa (ASTM C633)

Corrosion resistance: 30% longer life in 10% H₂SO₃ solution.

Q3: What is the particle shape and size range of the powder?

A3: Near-spherical particles made by plasma spheronization process, standard particle size 15-53μm (suitable for plasma spraying), support customized 5-25μm (HVOF) or 75-150μm (arc spraying).